A Grade 4 titanium was processed by equal-channel angular pressing (ECAP)–Conform and drawing to produce an ultrafine grain (UFG) size of ~180 nm. Some samples were tested in this condition (UFG-1) and others were annealed for 1 h at 623 K (UFG-2). The grain boundaries are in a non-equilibrium condition after processing, but the annealing equilibrates the boundaries without any increase in grain size. This leads to significant differences in the mechanical behavior of UFG-1 and UFG-2 when they are tested at 293 and 623 K.